{Title}: Effect of "fast"-crystallization and simultaneous glazing on physicochemical properties of lithium-disilicate CAD/CAM ceramic.
{Author}: Murillo-Gómez F;Murillo-Alvarado F;Vásquez-Sancho F;Avendaño E;Urcuyo R;
{Journal}: J Dent
{Volume}: 148
{Issue}: 0
{Year}: 2024 09 21
{Factor}: 4.991
{DOI}: 10.1016/j.jdent.2024.105257
{Abstract}: Evaluate the impact of a "fast" crystallization and simultaneous-glazing on the physicochemical properties of lithium-disilicate CAD/CAM-ceramic.<BR>Lithium-disilicate bars and crowns (IPS e.max CAD, Ivoclar-Vivadent) were divided into four groups (n = 30): WG/F (WG=with glaze/F=fast crystallization), NG/F (NG=no glaze), WG/C (C=conventional crystallization), and NG/C. A liquid/powder glaze system was used (IPS Ivocolor®, Ivoclar-Vivadent). Specimens were crystallized (Programat P310, Ivoclar-Vivadent) using the P161 program for C (approx. 20-25 min), and P165 for F (approx. 14-16 min). Bars (n = 30) underwent three-point bending tests (flexural strength-FS in MPa and modulus of elasticity-E in GPa) using a universal testing machine. Crowns were analyzed via scanning electron microscopy (SEM) after selective etching, and to Raman, FTIR-ATR, and X-ray diffraction (XRD) spectroscopies to assess chemical composition.<BR>For FS, both factors/interaction were statistically significant. C (427.48±42.41 MPa) showed significantly higher values than F (409.82±38.82 MPa). WG (398.32±29.80 MPa) exhibited significantly lower FS than NG (438.21±41.77 MPa). For E data, both factors/interaction were significant. NG (90.28±14.71 GPa) displayed higher E than WG (83.07±5.69 GPa), while C (90.08±12.98 GPa) exhibited higher E than F (83.46±9.40 GPa). NG/C showed the best results for both variables. F groups showed (SEM) porous surfaces and crack-like marks on crystals. FTIR, Raman and XRD spectra confirmed the typical composition of a lithium-disilicate glass ceramic, and some attenuated signals and structural variations (XRD) in WG.<BR>"Fast" crystallization and simultaneous-glazing produced weaker/less-rigid structures with irregular crystals and glassy phases. Simultaneous glazing may have hindered proper thermal distribution during crystallization.<BR>"Fast" crystallization and simultaneous glazing with non-recommended systems, can adversely affect the final properties of lithium disilicate restorations.