{Reference Type}: Journal Article
{Title}: Comprehensive Analysis of Wettability in Waterproofed Gas Diffusion Layers for Polymer Electrolyte Fuel Cells.
{Author}: Yoshimune W;Kato A;Yamaguchi S;Hibi S;Kato S;
{Journal}: ACS Appl Mater Interfaces
{Volume}: 0
{Issue}: 0
{Year}: 2024 Jul 4
{Factor}: 10.383
{DOI}: 10.1021/acsami.4c07867
{Abstract}: In polymer electrolyte fuel cells (PEFCs), the gas diffusion layer (GDL) is crucial for managing the flooding tolerance, which is the ability to remove the water produced during power generation from the assembled cell. However, an improved understanding of the properties of GDLs is required to develop effective waterproofing strategies. This study investigated the influence of the polytetrafluoroethylene (PTFE) content on the pore diameter, porosity, wettability, water saturation, and flooding tolerance of waterproofed carbon papers as cathode GDLs in PEFCs. The addition of minimal PTFE (∼6 wt %) to carbon paper provided external waterproofing, whereas internal waterproofing was achieved at a higher PTFE content (∼13 wt %). However, excessive PTFE (∼37 wt %) led to macropore collapse within the carbon paper, reducing fuel cell performance. Although PTFE addition was expected to improve the flooding tolerance, operando synchrotron X-ray radiography revealed that the water saturation level in carbon paper increased with increasing PTFE content. These findings provide a benchmark for assessing whether GDLs meet the flooding tolerance requirements of PEFCs and may be applicable to waterproofed GDLs in electrochemical devices for water and CO2 electrolysis.