{Reference Type}: Journal Article
{Title}: The effect of restorative material selection and cementation procedures on the durability of endocrowns in the anterior teeth: an in-vitro study.
{Author}: Samra N;Madina MM;El-Negoly SAE;Dawood L;
{Journal}: BMC Oral Health
{Volume}: 24
{Issue}: 1
{Year}: 2024 Jun 8
{Factor}: 3.747
{DOI}: 10.1186/s12903-024-04381-9
{Abstract}: OBJECTIVE: To investigate the fracture resistance and failure modalities of anterior endocrown restorations fabricated employing diverse ceramic materials, and bonded using various cementation methodologies.
METHODS: Forty maxillary central incisors were divided into two main groups based on the ceramic materials used; GroupI (Zir): zirconia endocrwons (Zolid HT+, Ceramill, Amanngirrbach) and GroupII (E-Max): e-max endocrowns (IPS e.max CAD, Ivoclar Vivadent). Both groups were further split into two subgroups depending on the cementation protocols; subgroup IA "ZirMDP": endocowns cemented with MDP primer + MDP resin cement, subgroup IB (ZirNon-MDP): cemented with MDP primer + non-MDP resin cement, subgroup IIA (E-maxMDP): cemented with MDP primer + MDP resin cement, subgroup IIB (E-maxNon-MDP): cemented with MDP primer + non-MDP resin cement. (n = 10/subgroup). Endocrowns were manufactured using CAD/ CAM. Teeth were subjected to 10,000 thermal cycles. The fracture test was performed at 45o with a palatal force direction until the fracture occurred. Test results were recorded in Newton. The failure mode was examined using a stereomicroscope. A One-way ANOVA test was utilized to compare different groups regarding fracture strength values. Tukey`s Post Hoc was utilized for multiple comparisons.
RESULTS: The comparative analysis of fracture strength across the diverse groups yielded non-significant differences, as indicated by a p-value exceeding 0.05. Nonetheless, an observable trend emerged regarding the mode of failure. Specifically, a statistically significant prevalence was noted in fractures localized within the endocrown/tooth complex below the cementoenamel junction (CEJ) across all groups, except for Group IIB, "E-max Non-MDP," where fractures within the endocrown/tooth complex occurred above the CEJ.
CONCLUSIONS: Combining an MDP-based primer with an MDP-based resin cement did not result in a significant effect on the anterior endocrown fracture strength.
CONCLUSIONS: Regardless of the presence of the MDP monomer in its composition, adhesive resin cement achieved highly successful fracture strength when used with MDP-based ceramic primers. Additionally, ceramic materials exhibiting elastic moduli surpassing those of dentin are discouraged due to their propensity to induce catastrophic fractures within the tooth structure.