%T Preparation of Water-Soluble Polyion Complex (PIC) Micelles with pH-Responsive Carboxybetaine Block.
%A Yokota K
%A Takahashi R
%A Ngan VT
%A Nishimura T
%A Kappl M
%A Fujii S
%A Yusa SI
%J Macromol Rapid Commun
%V 0
%N 0
%D 2024 Aug 1
%M 39090528
%F 5.006
%R 10.1002/marc.202400532
%X A dual zwitterionic diblock copolymer (M100C100) consisting of poly(2-(methacryloyloxy)ethyl phosphorylcholine) (PMPC, M) and poly(3-((2-(methacryloyloxy)ethyl) dimethylammonio) propionate) (PCBMA, C) is synthesized via reversible addition-fragmentation chain transfer (RAFT) polymerization. A double hydrophilic diblock copolymer (M100S100) consist of PMPC and anionic poly(3-sulfopropyl methacrylate potassium salt) (PMPS, S) is synthesized via RAFT. The degrees of polymerization of each block are 100. The charges of PMPC are neutralized intramolecularly. At neutral pH, the charges in PCBMA are also neutralized intramolecularly due to its carboxybetaine structure. Under acidic conditions, PCBMA exhibits polycation behavior as the pendant carboxy groups become protonated, forming cationic tertiary amine groups. PMPS shows permanent anionic nature independent of pH. Charge neutralized mixture of cationic M100C100 and anionic M100S100 in acidic aqueous solution forms water-soluble polyion complex (PIC) micelle owing to electrostatic attractive interactions. The core is composed of the cationic PCBMA and anionic PMPS blocks, with the PMPC blocks serving as shells that covered the core surface, forming spherical core-shell PIC micelles. Above pH 4 the pendant carboxy groups in PCBMA undergo deprotonation, transitioning to a zwitterionic state, thereby eliminating the cationic charge in PCBMA. Therefore, above pH 4 the PIC micelles are dissociated due to the disappearance of the charge interactions.