%0 Journal Article
%T Degradation of Polymer Films of Sodium Alginate during Prolonged Irradiation with X-ray under Ultra-High Vacuum.
%A Kabachkov EN
%A Baskakov SA
%A Shulga YM
%J Polymers (Basel)
%V 16
%N 14
%D 2024 Jul 20
%M 39065389
%F 4.967
%R 10.3390/polym16142072
%X Sodium alginate (NaAlg) is widely used as a food additive. To study the effect of irradiation with X-ray quanta with energies of 1253.6 eV and 1486.6 eV on the composition of NaAlg, thick films with a smooth surface were prepared, which did not differ in IR spectra from the original powders. The films were irradiated in a high vacuum (3 × 10-10 mbar) in the chamber of a Specs PHOIBOS 150 MCD9 XPS spectrometer with an X-ray source power of 150 W and an irradiation duration of up to 300 min, which significantly exceeded the time required to obtain an XPS spectrum. This made it possible to use XPS to monitor changes in the composition of the NaAlg surface directly during irradiation. As a result of the research, it has been established that NaAlg degrades with prolonged irradiation, which is accompanied by a significant decrease in the O/C ratio. When analyzing the dependence of the intensities of individual peaks in the C1s spectrum on the irradiation time, it was found that after 100 min of irradiation, a peak due to the carbonate group appears in the spectrum. The decomposition was also accompanied by a change in the color of NaAlg from white to yellow-brown. In the IR spectrum of the NaAlg film irradiated for 300 min, an absorption band was detected at 1910 cm-1, which is usually associated with the presence of allene groups.