%T Preparation of a high-performance conductive lignocellulose hydrogel by directly using non-detoxified bisulfite-pretreated corncob.
%A Wang P
%A Zheng T
%A Gan S
%A Yao J
%J Int J Biol Macromol
%V 275
%N 0
%D 2024 Aug 5
%M 38972648
%F 8.025
%R 10.1016/j.ijbiomac.2024.133695
%X Biomass-based hydrogels have become a research hotspot because of their better biocompatibility. However, the preparation of biomass hydrogels is complicated, and they often need to be modified by introducing other substances. In this study, corncob pretreated with bisulfite (125-185 °C) was used as a raw material to prepare lignocellulose hydrogels. The results showed that directly using the pretreated sample without the washing step lowered the total hydrogel costs while preserving the lignosulfonate (LS) produced during pretreatment. The best tensile (54.1 kPa) and compressive (177.7 kPa) stresses were obtained for the hydrogel prepared from non-detoxified pretreated corncob at 165 °C (NCH-165). The sulfonic acid groups in LS could enhance the interaction between plant cellulose, thus improving its mechanical properties. The capacitor assembled from NCH-165 achieved an energy density of 236.1 Wh/kg at a power density of 499.7 W/kg and a high coulombic efficiency of more than 99 % after 2000 charge/discharge cycles. In conclusion, the present study simplifies the pathway for the preparation of flexible, conductive, and anti-freezing hydrogels by directly utilizing a non-detoxified bisulfite-pretreated corncob.