%0 Journal Article
%T High-Performance Battery-Type Supercapacitors Based on Self-Oriented Growth of Nanorods/Nanospheres Composite Assembled on Self-Standing Conductive GO/CNF Frameworks.
%A Roy N
%A Rajasekhara Reddy G
%A Pallavolu MR
%A Nallapureddy RR
%A Dhananjaya M
%A Sai Kumar A
%A Banerjee AN
%A Min BK
%A Barai HR
%A Joo SW
%J ACS Appl Mater Interfaces
%V 0
%N 0
%D 2024 Jun 28
%M 38940603
%F 10.383
%R 10.1021/acsami.4c03109
%X MnOx-based materials have limited capacity and poor conductivity over various voltages, hampering their potential for energy storage applications. This work proposes a novel approach to address these challenges. A self-oriented multiple-electronic structure of a 1D-MnO2-nanorod/2D-Mn2O3-nanosphere composite was assembled on 2D-graphene oxide nanosheet/1D-carbon nanofiber (GO/CNF) hybrids. Aided by K+ ions, the MnO2 nanorods were partially converted to Mn2O3 nanospheres, while the GO nanosheets were combined with CNF through hydrogen bonds resulting in a unique double binary 1D-2D mixed morphology of MnO2/Mn2O3-GO/CNF hybrid, having a novel mechanism of multiple Mn ion redox reactions facilitated by the interconnected 3D network. The morphology of the MnO2 nanorods was controlled by regulating the potassium ion content through a rinsing strategy. Interestingly, pure MnO2 nanorods undergo air-annealing to form a mixture of nanorods and nanospheres (MnO2/Mn2O3) with a distinct morphology indicating pseudocapacitive surface redox reactions involving Mn2+, Mn3+, and Mn4+. In the presence of the GO/CNF framework, the charge storage properties of the MnO2/Mn2O3-GO/CNF composite electrode show dominant battery-type behavior because of the unique mesoporous structure with a crumpled morphology that provides relatively large voids and cavities with smaller diffusion paths to facilitate the accumulation/intercalation of charges at the inner electroactive sites for the diffusion-controlled process. The corresponding specific capacity of 800 C g-1 or 222.2 mAh g-1 at 1 A g-1 and remarkable cycling stability (95%) over 5000 cycles at 3 A g-1 were considerably higher than those of the reported electrodes of similar materials. Moreover, a hybrid supercapacitor device is assembled using MnO2/Mn2O3-GO/CNF as the positive electrode and activated carbon as the negative electrode, which exhibits a superior maximum energy density (∼25 Wh kg-1) and maximum power density (∼4.0 kW kg-1). Therefore, the as-synthesized composite highlights the development of highly active low-cost materials for next-generation energy storage applications.