%0 Journal Article
%T Synthesis, characterization and stability of crosslinked chitosan-maltodextrin pH-sensitive nanogels.
%A Fernández-Solís KG
%A Domínguez-Fonseca E
%A Martínez BMG
%A Becerra AG
%A Ochoa EF
%A Mendizábal E
%A Toriz G
%A Loyer P
%A Rosselgong J
%A Bravo-Anaya LM
%J Int J Biol Macromol
%V 274
%N 0
%D 2024 Aug 21
%M 38908642
%F 8.025
%R 10.1016/j.ijbiomac.2024.133277
%X Polysaccharide-based nanogels offer a wide range of chemical compositions and are of great interest due to their biodegradability, biocompatibility, non-toxicity, and their ability to display pH, temperature, or enzymatic response. In this work, we synthesized monodisperse and tunable pH-sensitive nanogels by crosslinking, through reductive amination, chitosan and partially oxidized maltodextrins, by keeping the concentration of chitosan close to its overlap concentration, i.e. in the dilute and semi-dilute regime. The chitosan/maltodextrin nanogels presented sizes ranging from 63 ± 9 to 279 ± 16 nm, showed quasi-spherical and cauliflower-like morphology, reached a ζ-potential of +36 ± 2 mV and maintained a colloidal stability for up to 7 weeks. It was found that the size and surface charge of nanogels depended both on the oxidation degree of maltodextrins and chitosan concentration, as well as on its degree of acetylation and protonation, the latter tuned by pH. The pH-responsiveness of the nanogels was evidenced by an increased size, owed to swelling, and ζ-potential when pH was lowered. Finally, maltodextrin-chitosan biocompatible nanogels were assessed by cell viability assay performed using the HEK293T cell line.