%0 Journal Article
%T The effects of monomer type, filler size, and filler content of three resin cements on the color stability of laminate veneers exposed to accelerated aging.
%A Alghazzawi TF
%J Dent Mater
%V 40
%N 8
%D 2024 Aug 19
%M 38902146
%F 5.687
%R 10.1016/j.dental.2024.06.001
%X <B>BACKGROUND: </B>Commercially available resin cements consist of various filler sizes, filler content and monomers, and it is unclear which of these factors have the greatest effect on the color stability of laminate veneers.<BR><B>OBJECTIVE: </B>To evaluate the color stability of lithium disilicate-reinforced laminate veneers inserted with three commercial resin cements with various filler sizes/contents and monomers upon accelerated aging.<BR><B>METHODS: </B>Veneers were fabricated and cemented on resin abutments using three commercially available resin cements comprised of two different monomers and varying filler sizes/contents: 1) triethylene glycol dimethacrylate, TEGDMA (RelyX™ Veneer = 0.6 µm/66 %, Calibra® Esthetic Light Cure =1.2 µm/65 %); and 2) urethane dimethacrylate, UDMA (Variolink Esthetic LC = 0.1 µm/38 %). A total of 60 specimens were fabricated (n = 20 for each cement). The relative number of particles (N) and relative surface area (A) were calculated for each filler size/content. Color coordinates (L*, a*, b*) were measured, and color change (ΔE00) was calculated after cementation and following aging at 150, 300, 450, and 600 h using xenon light. Differences in color coordinates and color change were determined using repeated measures ANOVA followed by Tukey's post hoc test (α = .05). A post-hoc power analysis was performed to confirm reliability of the results.<BR><B>RESULTS: </B>Based on a post-hoc power analysis of a repeated measures ANOVA with two between-factors and 1 within-factor, we had 89 % power to detect a difference of effect by cement type, 10 % power to detect a difference by shade, and 100 % power to detect a difference of effect by aging. The UDMA-based cement (0.1 µm/38 %) was least affected by aging, despite having the largest number of particles (N = 1010) and largest particle surface area (A = 7.02). The TEGDMA-based cements exhibited a significant color change, with 0.6 µm/66 % (A = 2.03, N = 8.12) producing a larger ΔE00 than 1.2 µm/65 % (A = 1.00, N = 1.00).<BR><B>CONCLUSIONS: </B>Among the commercial cements tested, UDMA-based resin (0.1 µm/38 %) provided better color stability than TEGDMA-based resin cements. The color change after aging was affected by the relative surface area and relative number of particles for the TEGDMA-based resin cement (0.6 µm/66 % and 1.2 µm/65 %), with a larger surface area and a higher relative number of particles, accelerated color change with aging. The present study demonstrates a novel approach to determine color stability for any resin cement with particulate filler.<BR><B>CONCLUSIONS: </B>The dental practitioner should be selective in choosing a commercial light cure cementation product for laminate veneers, as UDMA containing resin cement is more resistant to color changes over time than TEGDMA, regardless of the filler size/content.