%T Platinum-Iridium Alloy Nanoparticle Coatings Produced by Electrophoretic Deposition Reduce Impedance in 3D Neural Electrodes.
%A Ramesh V
%A Johny J
%A Jakobi J
%A Stuckert R
%A Rehbock C
%A Barcikowski S
%J Chemphyschem
%V 0
%N 0
%D 2024 Jun 6
%M 38842467
%F 3.52
%R 10.1002/cphc.202300623
%X Platinum-based neural electrodes, frequently alloyed with Ir or W, are routinely used to treat neurological disorders. However, their performance is impaired by an increase in impedance that compromises long-term implant functionality. Though there are multiple coating techniques available to address this issue, electrode, and base material often exhibit a compositional mismatch, which impairs mechanical stability and may lead to toxicological side effects. In this work, we coated Pt wire electrodes with ligand-free electrostatically stabilized colloidal Pt90Ir10, Pt90W10, and Pt50W50 alloy nanoparticles (NPs) matching electrode compositions using electrophoretic deposition (EPD) with direct-current (DC) and pulsed-DC fields in aqueous medium. The generated alloy NPs exhibit a solid solution structure as evidenced by HR-TEM-EDX and XRD, though additional WOx phases were identified in the Pt50W50 samples. Consequently, coating efficiency was also impaired in the presence of high W mass fractions in the alloy NPs. Characterization of the NP coatings by cyclic voltammetry and impedance spectroscopy yielded a significant reduction of the impedance in the Pt90Ir10 sample in comparison to the control coated with Pt NPs. The electrochemical surface area (ECSA) of the PtW alloy coatings, on the other hand, was significantly reduced.