%0 Journal Article
%T Synthesis of a novel Si-N-S flame retardant and its application on cotton cellulose biomacromolecule.
%A Tian J
%A Yu W
%A Pan J
%A Qi Z
%A Lin L
%A Wang J
%A Wang C
%J Int J Biol Macromol
%V 273
%N 0
%D 2024 Jul 30
%M 38823732
%F 8.025
%R 10.1016/j.ijbiomac.2024.132775
%X A novel flame retardant containing Si, N, and S elements, ((2-(triethoxysilyl)ethyl)thio)ethan-1-amine hydrochloride (TETEA), was synthesized via a click reaction and characterized using nuclear magnetic resonance spectroscopy (NMR) and fourier transform infrared spectroscopy (FTIR). Subsequently, the flame-retardant cotton fabric was fabricated by sol-gel method. The results indicated that TETEA was successfully loaded on cotton fabric and formed a uniform protective layer on the surface of cotton fabric, exhibiting excellent flame retardancy. The flame-retardant cotton fabric achieved limiting oxygen index (LOI) of 28.3 % and passed vertical combustion test without after-flame or afterglow time at TETEA concentration of 500 g/L. Thermogravimetric analysis revealed that the residual carbon content of the flame-retardant cotton fabric was much higher than that of the control under air and N2 conditions. Besides, the flame-retardant cotton fabric was not ignited in cone calorimeter test with an external heat flux of 35 kW/m2. The peak heat release rate and the total heat release decreased from 133.4 kW/m2 to 25.8 kW/m2 and from 26.46 MJ/m2 to 17.96 MJ/m2, respectively. This phosphorus-free flame retardant offers a simplified synthesis process without adverse environmental impacts, opening up a new avenue for the development environmentally friendly flame retardants compared to traditional alternatives.