%0 Journal Article
%T Synthesis of grafted bromoisobutyryl esterified starch using electron transfer atom transfer radical polymerization method with high-performance adhesion and film properties.
%A Li W
%A Zhang Z
%A Zhang X
%A Wang Y
%A Ruan F
%A Xing J
%J Int J Biol Macromol
%V 266
%N 0
%D 2024 May 8
%M 38641505
%F 8.025
%R 10.1016/j.ijbiomac.2024.131421
%X Nowadays, few investigations on the process parameters of grafted starch synthesized using electron transfer atom transfer radical polymerization (ARGET ATRP) and its applications in warp sizing and paper-making are presented. Therefore, this study aimed to survey the appropriate process parameters of bromoisobutyryl esterified starch-g-poly(acrylic acid) (BBES-g-PAA) synthesized by the ARGET ATRP, and also aimed to provide a new biobased BBES-g-PAA adhesive. The appropriate synthesis process parameters were 1.2, 0.32, and 0.6 in the molar ratios of vitamin C, CuBr2, and pentamethyldivinyltriamine to BBES, respectively, at 40 °C for 5 h. The BBES-g-PAA samples with a grafting ratio range of 4.63-14.14 % exhibited bonding forces of 57.8-64.6 N to wool fibers [55.5 N (BBES) and 53.8 N (ATS)], and their films showed breaking elongations of 3.29-3.80 % [2.74 % (BBES) and 2.49 % (ATS)] and tensile strengths of 29.1-25.4 MPa [30.4 MPa (BBES) and 34.7 MPa (ATS)]. Compared with BBES, significantly increased bonding forces and film elongations, and decreased film strengths for the BBES-g-PAA samples with grafting ratios ≥10.54 % were displayed (p < 0.05). The time (100-42 s) taken for the BBES-g-PAA films was significantly shorter than that of ATS (246 s) and BBES (196 s) films (p < 0.05), corresponding to better desizability.