%0 Journal Article
%T Study of okra pectin prepared by sweeping frequency ultrasound/freeze-thaw pretreatment on corrosion inhibition of ANSI 304 stainless steel in acidic environment.
%A Zhang L
%A Zhang A
%A Zhou S
%A Wang Q
%A Wang X
%A Ma H
%A Zhou C
%J Int J Biol Macromol
%V 253
%N 0
%D 2023 Dec 31
%M 37652320
%F 8.025
%R 10.1016/j.ijbiomac.2023.126587
%X Green and efficient metal corrosion inhibitors are very essential, and natural okra pectin (OP) can fulfill this need with rational use of resources. OP was prepared by water-alcohol extraction method after freeze-thaw pretreatment (FTP)/sweeping frequency ultrasound pretreatment (SFUP), and used for corrosion inhibition of ANSI 304 stainless steel (304 SS) in 1 M hydrochloric acid (HCl). The molecular weight, hydrodynamic diameter and monosaccharide composition of OP were analyzed to determine the factors on the corrosion inhibition of 304 SS. During SFUP of okra, the time-domain variation of ultrasound field was monitored by piezoelectric film sensor, its frequency-domain variation was monitored by a hydrophone, and analyzed respectively by oscilloscope and spectrum analyzer. Static weight-loss method, electrochemical and microscopic analyses were used to evaluate the corrosion inhibition efficiency of OP at temperatures (25, 30, 40, 50 °C) and concentrations (0, 0.2, 0.5, 1, 2 g·L-1) to optimize corrosion inhibition performance. It was found that OP by FTP and SFUP had higher corrosion inhibition efficiency on metals in acidic environment. According to static weight-loss method, the corrosion inhibition efficiency of OP with concentration of 2 g·L-1 (25 °C) was improved to 90.27 % in the FTP group and 93.53 % in the SFUP group, which 5.14 % and 8.93 % higher than Control (without pretreatment). Meanwhile, the corrosion inhibition efficiency decreased gradually as the temperature increased. OP corrosion inhibition performance fit Langmuir adsorption isothermal model as a mixed adsorption based on physical adsorption. It was a mixed inhibitor to protect 304 SS from corrosion.