%0 Journal Article
%T Effects of Translucency and Thickness of Lithium Disilicate-Reinforced Glass-Ceramic Veneers on the Degree of Conversion of a Purely Light-Curing Bonding Resin: An In Vitro Study.
%A Poca A
%A De Peretti Della Rocca K
%A Nasr K
%A Ducassé R
%A Canceill T
%J Polymers (Basel)
%V 15
%N 7
%D Mar 2023 24
%M 37050231
%F 4.967
%R 10.3390/polym15071617
%X The objective of this study was to evaluate the variations in the degree of conversion (DC) of a light-curing composite resin when the thickness or the translucency of lithium disilicate-enriched glass-ceramic veneers are modified. IPS e. max® CAD blocks of the MT-A2, LT-A2 and MO1 types were cut to obtain four slices with thicknesses ranging from 0.6 mm to 1 mm. A strictly light-curing composite resin (G-aenial Universal Injectable) was injected in the empty part of a silicone mold so that the veneer could then be inserted under digital pressure to the stop. A 40 s light cure (1400 mW/cm2) was then performed. Resin samples were analyzed using Fourier transform infrared (FTIR) spectroscopy. When the degree of translucency of the ceramic was modified, a decrease in the resin conversion rate was noted, but with a non-significant global p-value (p = 0.062). Interestingly, the degree of conversion of the light-curing composite resin was also modified when the ceramic's thickness increased, especially when it was over 1 mm (DC0.6 > DC0.7 > DC0.8 > DC1; p < 0.0001). This confirms that the degree of conversion of a bonding material is very dependent on the ceramic's thickness. Contradictory data are, however, found in the literature, where there are reports of an absence of a difference between the DC obtained with thicknesses of ceramics of 0.7 and 2 mm.