%T Comparative Evaluation of Effects of Laser Modalities on Shear Bond Strengths of Veneering Porcelains to Laser Sintered Substructures: An In Vitro Study.
%A Gorler O
%A Saygin AG
%J Photomed Laser Surg
%V 35
%N 6
%D Jun 2017
%M 28590838
暂无%R 10.1089/pho.2017.4299
%X OBJECTIVE: Laser modalities and direct metal laser sintering (DMLS) have a potential to enhance micromechanical bonding between dental super- and infrastructures. However, the effect of different manufacturing methods on the metal-ceramic bond strength needs further evaluation. We investigated the effect of surface treatment with Er:YAG, Nd:YAG, and Ho:YAG lasers on the shear bond strength (SBS) of high-fusion dental porcelains (Vita and G-Ceram) to infrastructures prepared with DMLS in vitro settings.
METHODS: Study specimens (n = 128) were randomly divided into study subsets (n = 8), considering treatment types applied on the surface of infrastructures, including sandblasting and selected laser modalities; infrastructure types as direct laser sintered (DLS) and Ni-Cr based; and superstructure porcelains as Vita and G-Ceram. The SBS test was performed to assess the effectiveness of surface modifications that were also examined with a stereo microscope.
RESULTS: Considering laser procedure types, the highest SBS values were obtained by Er:YAG laser, followed by, with a decreasing efficiency, Ho:YAG laser and sandblasting procedures, and Nd:YAG laser procedure (p < 0.05). Nd:YAG laser decreases the bonding of Vita and G-Ceram in all the infrastructures compared with sandblasting. Considering porcelains, the highest SBS values were obtained by Vita (p < 0.05). Considering infrastructures, the highest SBS values were obtained by DMLS procedure (p < 0.05). The laser procedures caused surface irregularities as revealed by the stereo microscopic examination.
CONCLUSIONS: In current experimental settings, Er:YAG laser applied to DLS infrastructure veneered with Vita porcelain increases bonding strength more distinctly, and Nd:YAG laser applied to Ni-Cr-based infrastructure veneered with G-Ceram porcelain alters bonding strength unfavorably.