Abstract:
White spot lesions (WSL) and incipient caries on enamel surfaces are the earliest clinical outcomes for demineralization and caries. If left untreated, the caries can progress and may cause complex restorative procedures or even tooth extraction which destroys soft and hard tissue architecture as a consequence of connective tissue and bone loss. Current clinical practices are insufficient in treating dental caries. A long-standing practical challenge associated with demineralization related to dental diseases is incorporating a functional mineral microlayer which is fully integrated into the molecular structure of the tooth in repairing damaged enamel. This study demonstrates that small peptide domains derived from native protein amelogenin can be utilized to construct a mineral layer on damaged human enamel in vitro. Six groups were prepared to carry out remineralization on artificially created lesions on enamel: (1) no treatment, (2) Ca2+ and PO43- only, (3) 1100 ppm fluoride (F), (4) 20 000 ppm F, (5) 1100 ppm F and peptide, and (6) peptide alone. While the 1100 ppm F sample (indicative of common F content of toothpaste for homecare) did not deliver F to the thinly deposited mineral layer, high F test sample (indicative of clinical varnish treatment) formed mainly CaF2 nanoparticles on the surface. Fluoride, however, was deposited in the presence of the peptide, which also formed a thin mineral layer which was partially crystallized as fluorapatite. Among the test groups, only the peptide-alone sample resulted in remineralization of fairly thick (10 μm) dense mineralized layer containing HAp mineral, resembling the structure of the healthy enamel. The newly formed mineralized layer exhibited integration with the underlying enamel as evident by cross-sectional imaging. The peptide-guided remineralization approach sets the foundation for future development of biomimetic products and treatments for dental health care.